GRM552B11H102KA01D datasheet(85/221 Pages) MURATA

85 / 221 page

Continued on the following page.

Preheat the capacitor at 120 to 150

°C for 1 minute. Immerse

the capacitor in a eutectic solder or Sn-3.0Ag-0.5Cu solder

solution at 270

±5°C for 10±0.5 seconds. Let sit at room

temperature for 24

±2 hours, then measure.

• Initial measurement.

Perform a heat treatment at 150+0/–10

°C for one hour and

then let sit for 24

±2 hours at room temperature. Perform the

initial measurement.

Resistance

to Soldering

Heat

Appearance

No marking defects

Capacitance

Change

Within

±7.5%

D.F.

W.V.: 25V min.; 0.025 max.

W.V.: 16V/10V max.; 0.035 max.

W.V.: 6.3V max.; 0.05 max.

I.R.

More than 10,000M

Ω or 500Ω · F (whichever is smaller)

Dielectric

Strength

No failure

Immerse the capacitor in a solution of ethanol (JIS-K-8101) and

rosin (JIS-K-5902) (25% rosin in weight proportion). Preheat at

80 to 120

°C for 10 to 30 seconds. After preheating, immerse in

eutectic solder solution for 2

±0.5 seconds at 230±5°C, or

Sn-3.0Ag-0.5Cu solder solution for 2

±0.5 seconds at 245±5°C.

Solderability of

Termination

75% of the terminations are to be soldered evenly

and continuously.

LLL/LLA/LLM Series Specifications and Test Methods (1)

Step

Temperature (

°C)

±2

–55

±3

±2

125

±3

±2

Char.

Temp. Range

(

°C)

–55 to +125

Reference

Temp.

°C

Cap.Change

Within

±15%

Within

±22%

Solder the capacitor to the test jig (glass epoxy board) in

the same manner and under the same conditions as (10). The

capacitor should be subjected to a simple harmonic motion

having a total amplitude of 1.5mm, the frequency being varied

uniformly between the approximate limits of 10 and 55Hz. The

frequency range, from 10 to 55Hz and return to 10Hz, should

be traversed in approximately 1 minute. This motion should be

applied for a period of 2 hours in each of 3 mutually

perpendicular directions (total of 6 hours).

Vibration

Resistance

Appearance

No defects or abnormalities

Capacitance

Within the specified tolerance

D.F.

W.V.: 25V min.; 0.025 max.

W.V.: 16V/10V max.; 0.035 max.

W.V.: 6.3V max.; 0.05 max.

Solder the capacitor to the test jig (glass epoxy board) using a

eutectic solder. Then apply 10N* force in parallel with the test

jig for 10

±1 sec. The soldering should be done either with an

iron or using the reflow method and should be conducted with

care so that the soldering is uniform and free of defects such as

heat shock.

*5N (LLL18 and LLA/LLM Series)

Adhesive Strength

of Termination

No removal of the terminations or other defect should occur.

The capacitance change should be measured after 5 min. at

each specified temperature stage.

The ranges of capacitance change compared with the 25

°C

value over the temperature ranges shown in the table should

be within the specified ranges.

• Initial measurement.

Perform a heat treatment at 150+0/-10

°C for one hour and then

set for 24

±2 hours at room temperature. Perform the initial

measurement.

Capacitance

Temperature

Characteristics

Dissipation Factor

(D.F.)

W.V.: 25V min.; 0.025 max.

W.V.: 16V/10V max.; 0.035 max.

W.V.: 6.3V max.; 0.05 max.

The capacitance/D.F. should be measured at 25

°C at the

frequency and voltage shown in the table.

Frequency: 1

±0.1kHz

Voltage: 1

±0.2Vrms

*For LLA185C70G474, the capacitance should be measured

unsing a voltage of 0.5

±0.1Vrms.

Capacitance

Within the specified tolerance

The insulation resistance should be measured with a DC voltage

not exceeding the rated voltage at 25

°C and 75%RH max. and

within 2 minutes of charging.

Insulation

Resistance

V0.047µF: More than 10,000MΩ

G0.047µF: More than 500Ω · F

C: Normal Capacitance

No failure should be observed when 250% of the rated voltage

is applied between the terminations for 1 to 5 seconds,

provided the charge/discharge current is less than 50mA.

Dielectric Strength

No defects or abnormalities

Using calipers

Dimensions

Within the specified dimension

Visual inspection

Appearance

No defects or abnormalities

The rated voltage is defined as the maximum voltage that may

be applied continuously to the capacitor.

When AC voltage is superimposed on DC voltage, VP-P or VO-P,

whichever is larger, should be maintained within the rated

voltage range.

Rated Voltage

See the previous pages.

Operating

Temperature

Range

R7, C7: –55 to +125

°C

No.

Test Method

Specifications

Item

!Note 1. This Specifications and Test Methods is downloaded from the website of Murata Manufacturing co.,ltd. Therefore, it's specifications are subject to change or our products in it may be discontinued without advance notice.

0. Please check with our sales representatives or product engineers before ordering.

2. This Specifications and Test Methods has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product

0. specifications before ordering.

LLL/LLR/LLA/LLM Series Specifications and Test Methods (1)

!Note • Please read rating and !CAUTION (for storage, operating, rating, soldering, mounting and handling) in this catalog to prevent smoking and/or burning, etc.

• This catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.

When no "*" is added in PNs table, please refer to LLL/LLR/LLA/LLM Series Specifications and Test Methods (1).

When "*" is added in PNs table, please refer to LLL/LLR/LLA/LLM Series Specifications and Test Methods (2).

• This PDF catalog is downloaded from the website of Murata Manufacturing co., ltd. Therefore, it’s specifications are subject to change or our products in it may be discontinued without advance notice. Please check with our

sales representatives or product engineers before ordering.

• This PDF catalog has only typical specifications because there is no space for detailed specifications. Therefore, please approve our product specifications or transact the approval sheet for product specifications before ordering.

!Note

C02E.pdf

10.12.20

GRM552B11H102KA01D Datasheet(PDF) 85 Page - Murata Manufacturing Co., Ltd.

GRM552B11H102KA01D Datasheet(HTML) 85 Page - Murata Manufacturing Co., Ltd.

Html Pages

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60 61 62 63 64 65 66 67 68 69 70 71 72 73 74 75 76 77 78 79 80 81 82 83 84 85 86 87 88 89 90 91 92 93 94 95 96 97 98 99 100 ...More

Datasheet Download

Link URL